[10up] Product Table Test: Polypropylene

Product Type

Applications

Polypropylene Product GradeTypeKey FeaturesMelt Flow RateFlexural ModulusTensile Strength at YieldTensile Elongation at YieldNotched Izod ImpactDTUL at 66 psi
CH005HomopolymerNSF 51 Listed, UL 94 HB, USP Class VI0.5 g/10 min230,000 psi5,100 psi11%1.5 ft-lb/in94°C
CH014HomopolymerUL 94 HB, USP <87>, USP <661.1>1.3 g/10 min215,000 psi5,000 psi11%1.1 ft-lb/in92°C
CH020-01HomopolymerBarefoot2 g/10 min215,000 psi5,000 psi11%1 ft-lb/in90°C
CH020XKHomopolymerHigh Crystallinity Barrier Property2.2 g/10 min255,000 psi5,200 psi8%1 ft-lb/in100°C
CH040HomopolymerNSF 51 Listed, High Crystallinity4 g/10 min255,000 psi5,200 psi8%0.8 ft-lb/in100ºC
CH120HomopolymerBarefoot, UL 94 HB12 g/10 min240,000 psiTensile Strength @ Yield : 5,000 psi8%0.7 ft-lb/in101°C
CH120LNHomopolymerUL 94 HB, DMF Listed, USP Class VI, USP <661.1>12 g/10 min280,000 psi5,250 psi7%1 ft-lb/in119°C
CH200LN-02HomopolymerDMF Listed, Nucleated. Antistat., USP <661.1>20 g/10 min270,000 psi5,550 psi7%0.8 ft-lb/in118ºC
CH350HomopolymerReactor Grade, DMF Listed, UL 94 HB35 g/10 min240,000 psi5,400 psi7.5%0.5 ft-lb/in101ºC
CH350LNHomopolymerReactor Grade, Nucleated. Anstistat35 g/10 min284,000 psi5,600 psi6.5%0.6 ft-lb/in120ºC
CH550LNHomopolymerHigh Flow. TWIM, Nucleated. Antistat.55 g/10 min279,000 psi5,600 psi6.5%0.5 ft-lb/in120°C
CM005Impact CopolymerExcellent Impact Properties in RT & -30°C, USP Class VI, GMW17178, Stellantis MS-DB-500 CPN4002 Color: Natural0.45 g/10 min175,000 psi3,650 psi15%No Break81ºC
CM010GImpact CopolymerPhosphorus Free0.9 g/10 min175,000 psi3,650 psi12%No Break81°C
CM015GImpact CopolymerPhosphorus Free1.4 g/10 min175,000 psi3,650 psi11%No Break81°C
CM017LImpact CopolymerBarefoot1.8 g/10 min165,000 psi3,700 psi13%7.1 ft-lb/in79°C
CM090LImpact CopolymerNSF 51 Listed10 g/10 min165,000 psi3,250 psi7%2.3 ft-lb/in79°C
CM120LNImpact CopolymerNucleated. Antistat, No-Break Izod Impact, UL 94 HB12 g/10 min170,000 psi3,250 psi6%No Break97°C
CM200LNImpact CopolymerUL 94 HB, Nucleated. Antistat., No-Break Izod Impact20 g/10 min137,000 psi2,850 psi9.5%No Break92°C
CM350LNImpact CopolymerNucleated. Antistat.35 g/10 min160,000 psi3,100 psi7.2%2.3 ft-lb/in96°C
CM350LN-01Impact CopolymerReactor Grade, Nucleated. Antistat.35 g/10 min190,000 psi3,500 psi6%1.2 ft-lb/in98°C
CM500LNImpact CopolymerNucleated. Antistat., High Flow. TWIM50 g/10 min160,000 psi3,150 psi6%2 ft-lb/in95°C
CR020CLRandom CopolymerClarified. Antistat.2 g/10 min156,000 psi4,200 psi14%4 ft-lb/in75°C
CR020NRandom CopolymerNucleated2 g/10 min155,000 psi4,130 psi13%2.4 ft-lb/in85°C
CR120CL-01Random CopolymerClarified. Antistat., DMF Listed12 g/10 min145,000 psi4,000 psi14%1.5 ft-lb/in70°C
CR120LNRandom CopolymerNucleated. Antistat.12 g/10 min145,000 psi4,000 psi13%1 ft-lb/in82°C
CR350CLRandom CopolymerReactor Grade, Clarified. Antistat., DMF Listed, USP <661.1>, USP Class VI35 g/10 min150,000 psi4,050 psi14%1.2 ft-lb/in73°C
CR350CL-02Random CopolymerClarified. Slip, DMF Listed35 g/10 min145,000 psi3,950 psi14%1.4 ft-lb/in71ºC
CR350CS-01Random CopolymerReactor Grade, Clarified. Slip, DMF Listed35 g/10 min150,000 psi4,050 psi14%1.2 ft-lb/in72°C
CR750CL-02Random CopolymerClarified. Antistat., High Flow. TWIM80 g/10 min150,000 psi4,050 psi14%1 ft-lb/in74°C
CR750CLSRandom CopolymerClarified. Lube, High Flow. TWIM80 g/10 min141,000 psi3,850 psi14%1 ft-lb/in68°C
CR750LNSRandom CopolymerNucleated. Lube, High Flow. TWIM80 g/10 min138,000 psi3,650 psi14%1 ft-lb/in70°C