| Polypropylene Product Grade | Type | Key Features | Melt Flow Rate | Flexural Modulus | Tensile Strength at Yield | Tensile Elongation at Yield | Notched Izod Impact | DTUL at 66 psi |
|---|---|---|---|---|---|---|---|---|
| CR350CS-01 | Random Copolymer | Reactor Grade, Clarified. Slip, DMF Listed | 35 g/10 min | 150,000 psi | 4,050 psi | 14% | 1.2 ft-lb/in | 72°C |
| CR350CL-02 | Random Copolymer | Clarified. Slip, DMF Listed | 35 g/10 min | 145,000 psi | 3,950 psi | 14% | 1.4 ft-lb/in | 71ºC |
| CR350CL | Random Copolymer | Reactor Grade, Clarified. Antistat., DMF Listed, USP <661.1>, USP Class VI | 35 g/10 min | 150,000 psi | 4,050 psi | 14% | 1.2 ft-lb/in | 73°C |
| CR120LN | Random Copolymer | Nucleated. Antistat. | 12 g/10 min | 145,000 psi | 4,000 psi | 13% | 1 ft-lb/in | 82°C |
| CR120CL-01 | Random Copolymer | Clarified. Antistat., DMF Listed | 12 g/10 min | 145,000 psi | 4,000 psi | 14% | 1.5 ft-lb/in | 70°C |
| CM350LN-01 | Impact Copolymer | Reactor Grade, Nucleated. Antistat. | 35 g/10 min | 190,000 psi | 3,500 psi | 6% | 1.2 ft-lb/in | 98°C |
| CM350LN | Impact Copolymer | Nucleated. Antistat. | 35 g/10 min | 160,000 psi | 3,100 psi | 7.2% | 2.3 ft-lb/in | 96°C |
| CH550LN | Homopolymer | High Flow. TWIM, Nucleated. Antistat. | 55 g/10 min | 279,000 psi | 5,600 psi | 6.5% | 0.5 ft-lb/in | 120°C |
| CH350LN | Homopolymer | Reactor Grade, Nucleated. Anstistat | 35 g/10 min | 284,000 psi | 5,600 psi | 6.5% | 0.6 ft-lb/in | 120ºC |
| CH200LN-02 | Homopolymer | DMF Listed, Nucleated. Antistat., USP <661.1> | 20 g/10 min | 270,000 psi | 5,550 psi | 7% | 0.8 ft-lb/in | 118ºC |