Polypropylene Product GradeTypeKey FeaturesMelt Flow RateFlexural ModulusTensile Strength at YieldTensile Elongation at YieldNotched Izod ImpactDTUL at 66 psi
CR750CL-02Random CopolymerClarified. Antistat., High Flow. TWIM80 g/10 min150,000 psi4,050 psi14%1 ft-lb/in74°C
CR750LNSRandom CopolymerNucleated. Lube, High Flow. TWIM80 g/10 min138,000 psi3,650 psi14%1 ft-lb/in70°C
CR750CLSRandom CopolymerClarified. Lube, High Flow. TWIM80 g/10 min141,000 psi3,850 psi14%1 ft-lb/in68°C
CR350CS-01Random CopolymerReactor Grade, Clarified. Slip, DMF Listed35 g/10 min150,000 psi4,050 psi14%1.2 ft-lb/in72°C
CR350CL-02Random CopolymerClarified. Slip, DMF Listed35 g/10 min145,000 psi3,950 psi14%1.4 ft-lb/in71ºC
CR350CLRandom CopolymerReactor Grade, Clarified. Antistat., DMF Listed, USP <661.1>, USP Class VI35 g/10 min150,000 psi4,050 psi14%1.2 ft-lb/in73°C
CM500LNImpact CopolymerNucleated. Antistat., High Flow. TWIM50 g/10 min160,000 psi3,150 psi6%2 ft-lb/in95°C
CM350LNImpact CopolymerNucleated. Antistat.35 g/10 min160,000 psi3,100 psi7.2%2.3 ft-lb/in96°C
CM200LNImpact CopolymerUL 94 HB, Nucleated. Antistat., No-Break Izod Impact20 g/10 min137,000 psi2,850 psi9.5%No Break92°C
CM120LNImpact CopolymerNucleated. Antistat, No-Break Izod Impact, UL 94 HB12 g/10 min170,000 psi3,250 psi6%No Break97°C