Compounding
CM200LN
Product Properties
COPYLENE® CM200LN is a super high Impact copolymer with a superior balance of stiffness and impact strength. The high melt flow allows for quick filling of molds and the anti-stat and nucleation facilitates fast cycle times. It is made with a non-phthalate catalyst.
| Typical Properties | Method | Value Unit |
|---|---|---|
| Physical | ||
| Melt Flow Rate (230˚C/2.16kg) | ASTM D 1238 | 20 g/10 min |
| Density-Specific Gravity | ASTM D 792 | 0.9 sp. gr. |
| Mechanical | ||
| Tensile Strength @ Yield (2 in/min) (50 mm/min) | ASTM D 638 | 2,850 psi 19.6 MPa. |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) (1 mm/min, 1% Secant, Procedure A) | ASTM D 790 | 137,000 psi 945 MPa. |
| Tensile Elongation @ Yield | ASTM D 638 | 9.5% |
| Impact | ||
| Notched Izod Impact (73 ˚F, Method A) (23 ˚C, Method A) | ASTM D 256 | No Break |
| Thermal | ||
| DTUL at 66 psi - Unannealed | ASTM D 648 | 92°C |
Applications
Consumer & Institutional Products (Outdoor Furniture)
Furniture, Housewares, Pet Products, Medical Products